For a lot of the CNC stuff I am doing, aluminum is one of the most
common metals used (primarily 6061, sometimes 7075 and similar),
followed by carbon steel.

Only about 325 grades of carbon steel...

Sometimes stainless steel, but stainless steel is both more expensive
and a pain to work with.

Work hardens into non-machinable stuff with a single instantaneous
wrong move. Moral:: if you start machining 303 you must continue until
it is done. with no stopping, using plenty of oil/coolant, and sharp
tooling.

>
Theoretically, one could melt and recast aluminum, but less likely to be
considered as "acceptable" (as the quality and metalurgy properties are
less likely to be the same as newly bought metal).

6061T6 is artificially aged (hardened and tempered) which you will not
get
by remelting 6061T6 and casting it. At best you get 6061T0 which is more
like
1100 aluminum than 6061T6 and especially not 6061T6 (or 6061T155 cast
version
of the extruded version of T6 after artificial aging.)

Say, if one goes and melts down the contents of their chip buckets (and
probably getting some ambiguous mixture of 6061 and 7075 and similar).

Mixing 6061 with 7075 is not going to give you an aluminum that has
any of the properties you want. The alloying elements are different
and incompatible.